♦ Aha Waya Wedding: ErNiCrMo-3, Inconel 625 TIG/MIG Waya
♦ MOQ:15kg
♦ Ụdị: MIG (15kgs / spool), TIG (5kgs / igbe)
♦ Nha:Dayameta 0.01mm-8.0mm
♦ Nha nkịtị:0.8MM / 1.0MM / 1.2MM / 1.6MM / 2.4MM / 3.2MM / 3.8MM / 4.0MM / 5.0MM
♦ Ụkpụrụ:Dabara na Asambodo AWS A5.14 ASME SFA A5.14
ErNiCrMo-3eji maka ịgbado ọkụ 625 (N06625) alloy, 20 alloy, 825,25-6Mo,9% Ni ígwè ma ọ bụ ndị ọzọ molybdenum ígwè, na-eji maka ịgbado ọkụ nke dị iche iche ihe na corrosion eguzogide surfacing nke ihe elu.
Magburu onwe n'ibu Njirimara na elu na ala okpomọkụ.Nguzogide corrosion siri ike, mgbawa corrosion nrụgide, pitting na corrosion azụ azụ n'ọtụtụ mgbasa ozi oxidation na mbelata.
C | Al | Si | Mn | Cr | Ni | Ti | Fe | S | Cu | Mo | P | Nb + Ta | Ndị ọzọ |
≤0.10 | ≤0.40 | ≤0.50 | ≤0.50 | 20.0-23.0 | ≥58.0 | ≤0.40 | ≤5.0 | ≤0.015 | ≤0.50 | 8.0 - 10.0 | ≤0.02 | 3.15 - 4.15 | ≤0.50 |
Dayameta | Usoro | Volt | Amps | Gas na-echebe | |
In | mm | ||||
0,035 | 0.9 | GMAW | 26-29 | 150-190 | Nyefe fesa100% Argon |
0,045 | 1.2 | 28-32 | 180-220 | ||
1/16 | 1.6 | 29-33 | 200-250 | ||
1/16 | 1.6 | GTAW | 14-18 | 90-130 | 100% Argon |
3/32 | 2.4 | 15-20 | 120-175 | ||
1/8 | 3.2 | 15-20 | 150-220 |
Ọnọdụ | Ike tensile MPa (ksi) | Mpụta Ike MPa (ksi) | Mgbatị% |
AWS reauirement | 760 (110) | Akọwapụtaghị ya | Akọwapụtaghị ya |
Nsonaazụ a na-ahụkarị dị ka welded | 790 (115) | 590 (85) | 35 |
Ọdịnaya ígwè dị ala, enwere ike iji ya na ịgbado ọkụ nke nickel-chromium molybdenum alloy,
Enwere ike iji ya maka mkpuchi na ịgbado nke ọla dị iche iche dị ka Ni-Cr-Mo alloy na igwe anaghị agba nchara na carbon steel.
Ọ nwere ezigbo nguzogide oxidation na mbelata gburugburu ebe obibi.
Ọdịnaya dị elu nke molybdenum na-enye ezigbo nrụgide na iguzogide pitting na creviccorrosion.
Ogige ngwa ERNiCrMo-3:
Ọ dabara adaba maka ịgbado ọkụ nke nickel-chrome-molybdenum alloy, dị ka Inconel625, Incoy 825, ma nwekwara ike iji maka ịgbado ọkụ na surfacing nke nickel-base alloy na igwe anaghị agba nchara dissimilar ihe.Enwere ike iji ya na gburugburu ebe obibi site na obere okpomọkụ ruo 540 ℃.